Name: LOCTITE PC9410
Brand: Henkel Corporation
SKU: LOCTITE PC9410

Main features

3 to 11 Minute Initial Set
-25 to 45 deg C Placement Range
17 to 21 N/mm^2 Strength After 2 Hours

Product Description

LOCTITE PC 9410 is a two-component magnesium phosphate-based system for concrete repair and grouting in potholes, loading areas, anchoring, and machinery-support work. Aggregate mixes with the activator to the required placement consistency without water as a diluent. Application and cure temperature is -25 to 45 deg C. ASTM C807 initial set time is 3 to 11 minutes and final set time is 15 to 22 minutes. Compressive strength develops from 17 to 21 N/mm^2 after 2 hours to 48 to 55 N/mm^2 after 28 days.

Key features

Setting Profile: Initial set time is 3 to 11 minutes by ASTM C807; final set time is 15 to 22 minutes.
-25 to 45 deg C Placement Range: Application and cure temperature is -25 to 45 deg C.
Compressive Strength Development: Compressive strength is 17 to 21 N/mm^2 after 2 hours and 48 to 55 N/mm^2 after 28 days.

Applications

Pothole and loading-area repair, concrete floor repair, machinery anchoring, and grouting of bedplates, soleplates, rails, bolts, and related concrete interfaces.

TDS, SDS & Technical Documents

Technical Specifications

General Properties

Appearance

Gray liquid

Additional Information

Technical properties

As supplied

Property	Value	Unit	Method / condition
Appearance	Gray liquid		Mixed to desired consistency
Activator-to-aggregate quantity	3.8 L to 20.4 kg		Approximate mixing quantity
Application and cure temperature	-25 to 45	deg C	During placement and cure
Initial set time	3 to 11	min	ASTM C807
Final set time	15 to 22	min	ASTM C807
Coverage	0.45	m^2	At 0.64 cm thickness per 4.54 kg