LOCTITE PC7363
Harmonization Code : 3403.19 | Lubricating Preparations (With 70% or More Petroleum Oils) For Automotive and Other Uses
Main features
- Non-Sag Ceramic-Tile Bonding
- 60-Minute Working Time
- 34.5 N/mm^2 Aluminum Lap Shear
Product Description
LOCTITE PC 7363 is a two-component epoxy paste adhesive for ceramic-tile installation on horizontal and vertical surfaces. The white-to-grayish paste mixes at a 1:1 resin-to-hardener ratio by volume. At 25 deg C, working time is 60 minutes and cure time is 12 hours. Cured material reaches Shore D 88 hardness and 96.6 N/mm^2 compressive strength. Lap shear is 34.5 N/mm^2 on acid-etched aluminum at a 0.125 mm gap. Typical dry service temperature is -29 to 93 deg C.
Key features
- Non-Sag Tile Bonding: The non-sag paste bonds ceramic tile on horizontal and vertical surfaces.
- 60-Minute Working Time: Working time is 60 minutes at 25 deg C before the 12-hour cure time at the same temperature.
- 34.5 N/mm^2 Aluminum Lap Shear: Lap shear is 34.5 N/mm^2 on acid-etched aluminum with a 0.125 mm gap by ISO 4587.
Applications
Ceramic-tile installation and bonding on horizontal and vertical surfaces.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Appearance
White to grayish paste
Appearance at room temperature.
Chemistry Type
Epoxy
Mix Ratio
1:1
The amount of a constituent divided by the total amount of all other constituents in a mixture
Additional Information
Technical properties
As supplied
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Resin viscosity | 1,800,000 to 2,700,000 | mPa s | Brookfield RV, spindle TF, 2.5 rpm, 25 deg C |
| Resin weight per gallon | 12.1 to 12.9 | lb/gal | As supplied |
| Hardener weight per gallon | 15.2 to 16.0 | lb/gal | As supplied |
| Mix ratio by volume | 1:1 | Resin:hardener; volume basis | |
| Working time | 60 | min | 25 deg C |
| Cure time | 12 | h | 25 deg C |
Technical properties
Cured material
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Shore hardness | 88 | Shore D | ISO 868, cured at 25 deg C |
| Compressive strength | 96.6 | N/mm^2 | ISO 604, cured at 25 deg C |
| Lap shear strength | 34.5 | N/mm^2 | ISO 4587, acid-etched aluminum, 0.125 mm gap, cured at 25 deg C |
| Typical dry service temperature | -29 to 93 | deg C | Cured adhesive |